Terluran® GP-22
丙烯腈丁二烯苯乙烯
INEOS Styrolution Group GmbH
產品說明:
Terluran® GP-22 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector.
FEATURES
| 總體 | ||||
| 材料狀態(tài) |
| |||
| 資料1 |
| |||
| 搜索 UL 黃卡 |
| |||
| 供貨地區(qū) |
| |||
| 特性 |
| |||
| 用途 |
| |||
| 形式 |
| |||
| 加工方法 |
| |||
| 多點數據 |
|
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 比重 | 1.04 | g/cm3 | ASTM D792,ISO 1183 |
| 熔流率（熔體流動速率） | ASTM D1238 | ||
| 200°C/5.0 kg | 1.5 | g/10 min | |
| 220°C/10.0 kg | 19 | g/10 min | |
| 溶化體積流率（MVR） | |||
| 230°C/3.8 kg | 4.80 | cm3/10min | ASTM D1238 |
| 220°C/10.0 kg | 19.0 | cm3/10min | ISO 1133 |
| 收縮率 | |||
| 流動 | 0.40 到 0.70 | % | ASTM D955 |
| -- | 0.40 到 0.70 | % | ISO 294-4 |
| 吸水率 | |||
| 飽和, 23°C | 1.0 | % | ASTM D570,ISO 62 |
| 平衡, 23°C, 50% RH | 0.22 | % | ISO 62 |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 洛氏硬度(R 級) | 103 |
| ASTM D785 |
| 球壓硬度 | 97.0 | MPa | ISO 2039-1 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量 | 2300 | MPa | ASTM D638,ISO 527-2 |
| 抗張強度(屈服, 23°C) | 45.0 | MPa | ASTM D638,ISO 527-2 |
| 拉伸應變 | |||
| 屈服, 23°C | 2.6 | % | ISO 527-2 |
| 斷裂 | 2.6 | % | ASTM D638 |
| 標稱拉伸斷裂應變(23°C) | 10 | % | ISO 527-2 |
| 彎曲模量 | 2300 | MPa | ASTM D790 |
| 彎曲強度 | 65.0 | MPa | ASTM D790,ISO 178 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強度 | ISO 179 | ||
| -30°C | 8.0 | kJ/m2 | |
| 23°C | 22 | kJ/m2 | |
| 簡支梁無缺口沖擊強度 | ISO 179 | ||
| -30°C | 100 | kJ/m2 | |
| 23°C | 180 | kJ/m2 | |
| 懸壁梁缺口沖擊強度 | |||
| -30°C | 59 | J/m | ASTM D256 |
| -18°C | 100 | J/m | ASTM D256 |
| 23°C | 300 | J/m | ASTM D256 |
| -30°C | 8.0 | kJ/m2 | ISO 180/A |
| 23°C | 26 | kJ/m2 | ISO 180/A |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa, 未退火 | 90.6 | °C | ASTM D648 |
| 0.45 MPa, 退火 | 104 | °C | ASTM D648 |
| 0.45 MPa, 退火2 | 99.0 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 77.8 | °C | ASTM D648 |
| 1.8 MPa, 退火 | 98.9 | °C | ASTM D648 |
| 1.8 MPa, 退火2 | 94.0 | °C | ISO 75-2/A |
| 維卡軟化溫度 | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 96.0 | °C | ISO 306/B50 |
| 線形熱膨脹系數 - 流動 | 8.0E-5 到 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 導熱系數 | 0.17 | W/m/K | DIN 52612 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 表面電阻率 | 1.0E+13 | ohms | IEC 60093 |
| 體積電阻率 | |||
| -- | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| 介電常數 | |||
| 1.00 mm, 1 MHz | 2.80 |
| ASTM D150 |
| 100 Hz | 2.90 |
| IEC 60250 |
| 1 MHz | 2.80 |
| IEC 60250 |
| 耗散因數 | IEC 60250 | ||
| 100 Hz | 4.8E-3 |
| |
| 1 MHz | 7.9E-3 |
|
| 光學性能 | 額定值 | 單位制 | 測試方法 |
| 黃度指數 | 13 | YI | DIN 6167 |
| 注射 | 額定值 | 單位制 |
|
| 干燥溫度 | 80.0 | °C | |
| 干燥時間 | 2.0 到 4.0 | hr | |
| 加工（熔體）溫度 | 220 到 260 | °C | |
| 模具溫度 | 30.0 到 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |